Speco Alloys Inc is one of the dominant Manufacturer, Exporter and Supplier of Titanium Alloy Grade 9 Round Bars in India. Titanium Grade 9 Round Bars is the most commonly accessible of all titanium alloys. Titanium Alloy Grade 9 Round Bars & Rods offers an astounding mix of high quality and strength. Titanium Grade 9 Round Bars & Rods has great welding and fabrication qualities.
They are utilized for a few applications, for example, in Aerospace, Marine, Chemical Processing, Medical, Consumer applications, Transportation, etc. Otherwise called UNS R56320 Round Bars, our Titanium Alloy Grade 9 Round Bars and Rods are open to our significant clients in various scope of measurements, thicknesses and sizes in customized structure furthermore at very moderate rates.
| Standard | ASTM B348 / ASME SB348, AMS 4976, AMS 4956 |
|---|---|
| Werkstoff Nr | 3.7195 |
| Grade | Titanium Grade 9 (UNS No. R56320) |
| Size | Dia6.0-200mm x Length1000-6000mm |
| Length | 2000mm – 5800mm |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc |
| Surface | Hot Rolled Pickled or Sand Blasting Finished, Cold Drawn, Bright, Polished, Hairline |
| Conditon | Cold Drawned Pulished Cold Drawn Centreless Ground & Polished. |
| Application | Chemical process, Food processing, Petrochemical, Pollution control, Pulp and Paper, Refining |
| Standard | Type of pipe | Grade | Al | Ti | V |
|---|---|---|---|---|---|
| max | max | max | |||
| UNS R56320 | SMLS & WELDED | 9 | 3 | 95 | 2.5 |
| Hardness, Brinell | 256 | 256 | Estimated from Rockwell C |
|---|---|---|---|
| Hardness, Knoop | 278 | 278 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 24 | 24 | annealed |
| Hardness, Vickers | 280 | 280 | Estimated from Brinell. |
| Tensile Strength, Ultimate | 89900 MPa | 620 psi | |
| Tensile Strength, Yield | 500 MPa | 72500 psi | |
| Elongation at Break | 15 % | 15 % | |
| Modulus of Elasticity | 100 Gpa | 14500 ksi | |
| Compressive Yield Strength | 105 GPa | 100000 ksi | In Tension |
| Notched Tensile Strength | 790 MPa | 115000 psi ksi | |
| Poisson's Ratio | 0.3 | 0.3 | |
| Charpy Impact | 86 J | 63.4 ft-lb | V-notch |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Fatigue Strength | 280 MPa | 40600 psi | 50,000 cycles. Kt (stress concentration factor) = 1.8 |
| Physical Properties | Metric | English |
|---|---|---|
| Density | 4.48 g/cc | 0.162 lb/in³ |
| Electrical Resistivity | 0.000127 ohm-cm | 0.000127 ohm-cm |
|---|
| CTE, linear 20°C | 9.61 µm/m-°C | 5.34 µin/in-°F | 20-95ºC |
|---|---|---|---|
| CTE, linear 250°C | 9.86 µm/m-°C | 5.48 µin/in-°F | 20-315ºC; 9.67 in range 20-205ºC |
| CTE, linear 500°C | 9.97 µm/m-°C | 5.54 µin/in-°F | Average over the range 20-540ºC |
| Specific Heat Capacity | 0.525 J/g-°C | 0.125 BTU/lb-°F | Typical value for titanium alloys.Heat Capacity at 540ºC is 0.67 J/g-ºC |
| Thermal Conductivity | 8.3 W/m-K | 57.6 BTU-in/hr-ft²-°F | Value at 315ºC is 11.8 W/m-ºC |
| Melting Point | Max 1700 °C | Max 3090 °F | Liquidus |
| Liquidus | 1700 °C | 3090 °F | |
| Beta Transus | 935 °C | 1720 °F |
Speco Alloys Inc exports TITANIUM GR 9 ROUND BARS & RODS MANUFACTURER AND EXPORTER to Dubai, Sharjah, Abhdhabi, Oman, Qatar, Saudi Arabia, Kuwait, Iran, Iraq, Malaysia, Indonesia, Norway, Nigeria, Algeria, Egypt, Libya, Brazil, Angola, Guinea, Mozambique, Tanzania, Venezuela, Canada, Ecuador, Ghana, Vietnam, Trinidad And Tobago, Thailand, Korea, Taiwan, Australia, Italy, France, Spain, Russia, Germany & Azerbaijan countries.